Change of Mechanical Properties of Bars in the Process of Deformation by Combined Method
Volokitina I.E. Volokitin A.V.
1 September 2024G.V. Kurdyumov Institute for Metal Physics of N.A.S. of Ukraine
Metallofizika i Noveishie Tekhnologii
2024#46Issue 9845 - 850 pp.
A new combined deformation technology combining radial-shear broaching and drawing technology is developed in this work, which makes it possible to improve the mechanical and operational properties of carbon-steel bars. As a result, during three straining cycles, the average value of microhardness in the central zone is of 2085 MPa, in the neutral zone, it is of 2505 MPa, and in the surface zone, it is of 2915 MPa. In addition, the strength properties are increased by almost 2 times, the plastic characteristics are reduced not much, but remain at a fairly good level for steel 45 due to obtaining gradient micro-structure during straining.
bar , drawing , radial-shear broaching , severe plastic defor-mation , steel
Text of the article Перейти на текст статьи
Karaganda Industrial University, Republic Ave. 30, Temirtau, 101400, Kazakhstan
Karaganda Industrial University
10 лет помогаем публиковать статьи Международный издатель
Книга Публикация научной статьи Волощук 2026 Book Publication of a scientific article 2026