FATIGUE PROPERTIES AND TRIBOLOGICAL TESTS OF AISI 316 STEEL AFTER HIGH PRESSURE TORSION
Volokitin A. Volokitina I. Naizabekov A. Kuis D. Lezhnev S. Panin E.
2023University of Chemical Technology and Metallurgy
Journal of Chemical Technology and Metallurgy
2023#58Issue 2412 - 419 pp.
The influence of the high pressure torsion process in the new die on the fatigue properties of AISI 316 corrosionresistant steel was investigated. Eight deformation cycles was carried out at cryogenic and ambient temperatures. It was revealed that the fatigue strength of both samples increases due to the structure grinding and twinning in austenite during deformation by high pressure torsion, partially martensitic transformation and an increase in the proportion of large-angle boundaries during cyclic deformation. The main factor of the higher fatigue limit of AISI 316 steel after deformation at cryogenic temperature compared to ambient temperature is a more intensive microstructure grinding and the presence of an increased proportion of large-angle boundaries and the course of a more complete martensitic transformation.
cryogenic conditions , fatigue properties , high pressure torsion , severe plastic deformation , tribology
Text of the article Перейти на текст статьи
Karaganda State Industrial University, Republic av. 30, Temirtau, 101400, Kazakhstan
Rudny Industrial Institute, 50 let Oktyabrya str. 38, Rudny, 111500, Kazakhstan
Belarusian State Technological University, Sverdlova 13a, Minsk, 220006, Belarus
Karaganda State Industrial University
Rudny Industrial Institute
Belarusian State Technological University
10 лет помогаем публиковать статьи Международный издатель
Книга Публикация научной статьи Волощук 2026 Book Publication of a scientific article 2026