WEAR OF 16MnCrS5 STEEL SURFACE LAYERS IN THE PULSING CONTACT LOADS
Stepankin I. Kuis D. Pozdnyakov E. Naizabekov A. Lezhnev S. Panin E.
2023Faculty of Metallurgy
Metalurgija
2023#62Issue 3-4437 - 439 pp.
Approaches to actualizing the use of modern alloy steels that are in demand in the Eurasian technological space are proposed. According to the criterion of resistance to contact fatigue, quantitative indicators of wear of the surface-hardened layers of steel 16MnCrS5 were revealed. With the contact stress amplitude up to 950 MPa, the composite material of carbonized and nitrocemented layers is characterized by a period of high resistance with minimal mani-festations of structural hardening by the mechanism of softening of the material. The obtained composite material with carbonized and nitrocemented layers is characterized by a period of high resistance up to 15 000 cycles.
16MnCrS5 , layers on surface , pulsing contact loads , thermal treatment , wear
Text of the article Перейти на текст статьи
Belorusneft, Gomel, Belarus
Rudny Industrial Institute, Rudny, Kazakhstan
Belaru-sian State Technological University, Minsk, Belarus
Pavel Sukhoi State Technical University of Gomel, Gomel, Belarus
Karaganda Industrial Univer-sity, Temirtau, Kazakhstan
Belorusneft
Rudny Industrial Institute
Belaru-sian State Technological University
Pavel Sukhoi State Technical University of Gomel
Karaganda Industrial Univer-sity
10 лет помогаем публиковать статьи Международный издатель
Книга Публикация научной статьи Волощук 2026 Book Publication of a scientific article 2026