Effect of Carbon and Cooling Rate on the Structure of Hypereutectic High Chromium Cast Iron in the Cast State and after Heat Treatment
Panichkin A. Kenzhegulov A. Mamaeva A. Uskenbayeva A. Kshibekova B. Imbarova A. Alibekov Z.
December 2023Multidisciplinary Digital Publishing Institute (MDPI)
Journal of Composites Science
2023#7Issue 12
The article presents experimental data on the changes in the structural parameters and properties of castings from high-chromium cast iron G-X300CrMo27-1 depending on the carbon content, which ranged from 2.8 to 4.5 wt. %. Castings were obtained under cooling conditions with two cooling rates—0.083–0.117 °C/s and 4.67–5 °C/s. Changes in the structure and properties of these castings after destabilizing annealing and subcritical heat treatment were assessed. Changes in carbon concentration and cooling rate in the crystallization interval have a significant effect on the sizes of primary carbides (Cr, Fe)7C3, and on the fraction of eutectic carbides. The microprobe analysis results indicating the effects of cooling rate on the composition of phases in cast iron castings with carbon contents of 4.2 wt. % are presented. The offset value of the crystallization onset temperature and eutectic point with an increase in the cast iron melt cooling rate from 0.083 to 0.83 °C/s is shown. The changes found in the properties of castings with increases in carbon concentration and cooling rate cannot be unambiguously explained by the transformation of the structure of primary and eutectic carbides and changes in the elemental composition of phases. The composition and condition of the matrix has a significant effect on the hardness, bending strength and abrasion resistance of castings. It is suggested that internal stresses arising in primary and eutectic carbides affect the properties of castings in the cast and heat-treated state.
abrasive wear resistance , carbon content , cooling rate , eutectic high chromium cast iron , hardness , strength , structure
Text of the article Перейти на текст статьи
The Institute of Metallurgy and Ore Beneficiation, JSC, Satbayev University, NJSC, Almaty, 050013, Kazakhstan
The Institute of Metallurgy and Ore Beneficiation
10 лет помогаем публиковать статьи Международный издатель
Книга Публикация научной статьи Волощук 2026 Book Publication of a scientific article 2026