SYNTHESIS OF COPOLYMERS FOR PROTECTIVE COATINGS
Merkulov V. Ulyeva G. Akhmetova G. Volokitin A.
2024University of Chemical Technology and Metallurgy
Journal of Chemical Technology and Metallurgy
2024#59Issue 3639 - 646 pp.
Copolymers were obtained in this work and the methodology for their synthesis was worked out. Various fillers were selected for the polymer coating. Resulting copolymers have good adhesion required for composite protective coatings. An experiment was conducted to determine the corrosion resistance of metals coated with copolymers when exposed to aggressive environments, as well as to determine the hardness and thickness of the polymer coatings obtained. It was found that the polymer coating filled with bronze powder, despite the small thickness of 43.4 μm, has the best adhesion and corrosion properties, as well as having the highest hardness values of 80.5 HB. Such physical and mechanical properties of polymer coatings allow them to be used as protective coatings for metal products working under the influence of aggressive media.
copolymer , copolymer synthesis , polymer , polymer coating , protective coating
Text of the article Перейти на текст статьи
Karaganda Industrial University, Republic Ave. 30, Temirtau, 101400, Kazakhstan
“ArcelorMittal Temirtau” Corporation, 1 Republic Ave., Temirtau, 101400, Kazakhstan
Karaganda Industrial University
“ArcelorMittal Temirtau” Corporation
10 лет помогаем публиковать статьи Международный издатель
Книга Публикация научной статьи Волощук 2026 Book Publication of a scientific article 2026