Thermodynamics of a Karatau and Aktobe phosphorites mixture interaction when producing phosphorus, calcium carbide and ferrosilicon
Термодинамическая картина взаимодействия смеси фосфоритов Каратау и Актобе с получением фосфора, карбида кальция и ферросилиция
Shevko V.M. Badikova A.D. Uteyeva R.A. Lavrov B.A. Amanov D.D.
2024Tomsk Polytechnic University, Publishing House
Bulletin of the Tomsk Polytechnic University, Geo Assets Engineering
2024#335Issue 1162 - 173 pp.
Relevance. The need to increase the level of comprehensive use of phosphorites during their electrothermal processing and to reduce the amount of slag waste generated during phosphorus production, polluting the environment. Aim. To conduct computer thermodynamic modeling of the effect of temperature and amount of iron on technological parameters of interaction of a Karatau and Aktobe phosphorites mixture with carbon and iron to produce phosphorus, calcium carbide and ferrosilicon. Objects. Phosphorites of the Karatau and Aktobe phosphorite-bearing basins. Methods. Thermodynamic computer modeling using the HSC Chemistry 6.0 software; rotatable second-order experiment planning technique; geometric optimization of technological parameters. Results. It has been established that depending on temperature in the mixture of Karatau and Aktobe phosphorites with carbon and iron, they participate in interaction: CaSiO3, SiO2, Si, SiC, SiO(g), MgSiO3, Al2SiO5, Na2SiO3, Ca(g), CaO, CaC2, CaF2, CaS, Fe, FeSi, FeSiO3, FeP, Fe2P, Fe3P, FeP2, FeO, Fe3Si; Ca3(PO4)2, P2(g), P4(g). An increase in iron amount leads to an increase in the degree of silicon extraction into the alloy, and at 2000°C reduces the extraction degree of calcium in CaC2 and the silicon concentration in the alloy. Branded calcium carbide with a volume of more than 230 dm3/kg and ferrosilicon FeSi25 are formed from a mixture of phosphorites, carbon and iron at 2077…2088°C in the presence of 20…21.4% iron and 43% carbon (in this case, phosphorus is completely distilled off into the gas phase). Using our proposed method of electric smelting of phosphorites with phosphorus distillation and associated production of ferroalloy, in comparison with the traditional method, the indicator of integrated use of raw materials increases from 43.9 to 62.7…73.6%, that is 1.43…1, 67 times. The proposed processing technology helps to increase active reserves of phosphorites and bring lowgrade phosphorites of the Aktobe basin into production.
calcium carbide , carbon , ferrosilicon , iron , mixture of phosphorites , phosphorus , rototable planning , temperature , thermodynamic modeling
Text of the article Перейти на текст статьи
M. Auezov South Kazakhstan University, Shymkent, Kazakhstan
Petersburg State Institute of Technology, Saint Petersburg, Russian Federation
M. Auezov South Kazakhstan University
Petersburg State Institute of Technology
10 лет помогаем публиковать статьи Международный издатель
Книга Публикация научной статьи Волощук 2026 Book Publication of a scientific article 2026