Study of Properties of Manganese-Containing Waste Processing Product as a Low-Carbon Steel Corrosion Inhibitor in Neutral Aqueous Media
Raimbekova A.S. Kapralova V.I. Kozlovskiy A.L. Kubekova S.N. Zhussupova L.A. Rysbekov K.
June 2025Engineered Science Publisher
ES Energy and Environment
2025#28
The inhibitory properties of the product obtained from manganese ore sampled from Zhairem deposit were studied on low-carbon steel (St3) in an aqueous medium. Standard gravimetric method and electrochemical measurements were used. It is shown that calcium-manganese phosphate product with composition СаО:MnO:Р2О5 (1.00:0.11:1.54) and the phosphate content from phosphorus pentoxide (73.64±1.33, wt.%), reduces the corrosion rate of steel St3 in the entire studied concentration range from 1 to 100 mg/L of Р2О5. In contrast to the well-known sodium polyphosphate inhibitor, it has been established that anti-corrosion treatment of water with a calcium-manganese phosphate inhibitor reduces the rate of accumulation of salt rust deposited on the steel surface. This was obtained to be practically zero at a concentration of 50 mg/L of P2O5. The results of electrochemical tests were confirmed by noting and calculating polarization curves of gravimetric measurements. During the study of the surface morphology of steel samples after being exposed to inhibitor solutions using scanning electron microscopy (SEM) and energy-dispersive analysis, the formation of uniform coatings consisting of compounds of calcium, manganese, iron and phosphorus was established. IR spectroscopic studies confirmed the formation of a protective coating in calcium-manganese solutions consisting of calcium, iron, and possibly manganese hydrodiphosphates.
Carbon steel , Corrosion , Corrosion rate , Degree of protection , Inhibitor , Inhibitory properties
Text of the article Перейти на текст статьи
Department of Chemical Processes and Industrial Ecology, Mining and Metallurgical Institute named after O.A. Baikonurov, Satbayev University, 22 Satbayev Str, Almaty, 050013, Kazakhstan
Solid State Physics Laboratory, Astana branch of the Institute of Nuclear Physics, Abylay khan st. 2/1, Astana, 010008, Kazakhstan
Department of Biology, Geography and Chemistry, Korkyt Ata Kyzylorda University, 29A Aiteke Bi Str, Kyzylorda, 120000, Kazakhstan
Mining and Metallurgical Institute named after O.A. Baikonurov, Satbayev University, 22 Satbayev Str, Almaty, 050013, Kazakhstan
Department of Chemical Processes and Industrial Ecology
Solid State Physics Laboratory
Department of Biology
Mining and Metallurgical Institute named after O.A. Baikonurov
10 лет помогаем публиковать статьи Международный издатель
Книга Публикация научной статьи Волощук 2026 Book Publication of a scientific article 2026