Structure and Phase Composition of the Products Derived from Vacuum–Thermal Treatment of a Tellurium-Containing Middling
Nitsenko A. Linnik X. Volodin V. Trebukhov S. Sukurov B. Tuleutay F. Dzhienalyev T.
October 2025Multidisciplinary Digital Publishing Institute (MDPI)
Materials
2025#18Issue 19
In this paper, the results from a study of the products obtained by vacuum–thermal processing of industrial copper telluride in an inert atmosphere at a pressure of 66 Pa and a temperature of 1100 °C are presented. The residue obtained mainly consisted of the copper(I) oxide phase. The condensate was represented by the phases CuTe2O5, CuO·CuTeO3, TeO2, SiO2, and CuTe2Cl. The vapor phase condensed in four temperature zones, each represented by a different phase composition. A monophase of tellurium oxide was identified in the condensate at temperatures of 150 to 270 °C. The obtained data contribute to expanding scientific knowledge and form the basis for developing a new, environmentally safe method of processing tellurium-containing middling. The creation of new technologies promotes increased efficiency of tellurium recovery and reduces environmental risks.
condensate , copper telluride , phase composition , vacuum
Text of the article Перейти на текст статьи
Institute of Metallurgy and Ore Beneficiation JSC, Satbayev University, Almaty, 050010, Kazakhstan
Institute of Metallurgy and Ore Beneficiation JSC
10 лет помогаем публиковать статьи Международный издатель
Книга Публикация научной статьи Волощук 2026 Book Publication of a scientific article 2026