Insight Into the Role of Fiber Diameter on Electrospun Polysulfone Mats
Khezri Z. Pirsalami S. Avaji S. Mousavi S.H. Riazi M.
15 December 2025John Wiley and Sons Inc
Journal of Polymer Science
2025#63Issue 245361 - 5371 pp.
Fiber electrospun mats created using cylindrical collectors have been extensively studied as effective membranes for water treatment. However, the relationships between the properties of electrospun mats and the characteristics and performance of membranes are not well-established. This research examined two samples with average fiber diameters of 1.8 ± 0.49 μm and 0.47 ± 0.26 μm, which were evaluated as supporting substrates for the separation of MgSO4 ions. The variation in fiber diameter resulted from consistent conditions of voltage, distance, and collector rotation speed, while the injection rates were different, set at 2 mL/h and 0.8 mL/h, respectively. The resulting thin-film composite (TFC) membrane consists of three layers: the first layer is a mesh polyester that underlies a middle hydrophobic electrospun support layer made from a 20 wt.% polysulfone solution. The third layer is a polyamide layer created through interfacial polymerization, involving a reaction between piperazine (PIP) monomers at a concentration of 2% by weight and trimesoyl chloride (TMC) monomers at a concentration of 0.2% by weight. Due to its hydrophobic nature, PSU repels water monomers from its surface during polymerization. Consequently, surface modification using plasma treatment alters the surface characteristics from hydrophobic to hydrophilic, resulting in the formation of a superior polyamide layer. The results indicate that membranes with larger fiber diameters exhibit a rougher texture. Additionally, the increased void space between the fibers in these membranes leads to an increase in pure water flux that is 92% higher compared to membrane samples with smaller fiber diameters; this higher flux is due to larger pore size. Furthermore, membranes with smaller fiber diameters possess a finer pore structure, resulting in a polyamide layer with fewer defects than membranes with larger fibers. This improved structure achieved a separation efficiency of 68% ± 1.02% for MgSO4, while the membrane with an average fiber diameter of 1.80 ± 0.49 μm demonstrated a separation rate of 20% ± 2.26%. These findings provide a step forward in the development of a theoretical framework for engineering TFC membranes with electrospun mats as supports.
electrospinning , fiber diameter , membrane , water treatment
Text of the article Перейти на текст статьи
Separation Processes and Nanotechnology Lab, Faculty of Caspian, College of Engineering, University of Tehran, Tehran, Iran
Enhanced Oil Recovery (EOR) Research Center, IOR/EOR Research Institute, Shiraz University, Shiraz, Iran
Department of Materials Engineering, Shiraz University, Shiraz, Iran
School of Mining and Geosciences, Nazarbayev University, Astana, Kazakhstan
Separation Processes and Nanotechnology Lab
Enhanced Oil Recovery (EOR) Research Center
Department of Materials Engineering
School of Mining and Geosciences
10 лет помогаем публиковать статьи Международный издатель
Книга Публикация научной статьи Волощук 2026 Book Publication of a scientific article 2026