Thermodynamics and Electrophysics of New LaCaCuZnMnO6 Copper–Zinc Manganite of Lanthanum and Calcium
Kasenov B.K. Kasenova S.B. Sagintaeva Z.I. Kuanyshbekov E.E. Mukhtar A.A. Kakenov K.S.
August 2022Pleiades Publishing
High Temperature
2022#60Issue 4474 - 478 pp.
Abstract: Copper–zinc lanthanum and calcium manganite LaCaCuZnMnO6 was synthesized from oxides of lanthanum(III), copper(II), zinc(II), manganese(III), and calcium carbonate in the temperature range 1073–1473 K. Nanostructured particles were obtained by grinding the material in a vibratory mill. The heat capacity of the compound was studied in the range of 298.15–673 K on an IT-S-400 calorimeter. On dependence curve (Formula presented.) at 598 K, an anomalous jump in heat capacity was detected. The temperature dependences of the electrical resistance and relative permittivity were studied on an LCR-781 setup (Taiwan) at 293–483 K and at frequencies of 1, 5, and 10 kHz. A semiconductor character of the conductivity was established. At 483 K, an anomalously high value of the permittivity was revealed at all studied frequencies.
Text of the article Перейти на текст статьи
Zh. Abishev Chemical–Metallurgical Institute, Karaganda, 100009, Kazakhstan
Karaganda Economic University of Kazpotrebsoyuz, Karaganda, 100000, Kazakhstan
Zh. Abishev Chemical–Metallurgical Institute
Karaganda Economic University of Kazpotrebsoyuz
10 лет помогаем публиковать статьи Международный издатель
Книга Публикация научной статьи Волощук 2026 Book Publication of a scientific article 2026