Thermodynamic and Electrophysical Properties of New Neodymium and Lithium Nickelite-Manganite NdLi2NiMnO5
Kasenov B.K. Sagintaeva Z.I. Kasenova S.B. Kuanyshbekov E.E. Nukhuly A. Mukhtar A.A.
October 2025Pleiades Publishing
Russian Journal of Physical Chemistry A
2025#99Issue 102423 - 2430 pp.
Abstract: Nickelite-manganite with a composition of NdLi2NiMnO5 has been synthesized by solid-phase interaction of oxides Nd2O3, NiO, Mn2O3, and Li2CO3 in the range of 600–1250°C. As shown by X-ray diffraction methods, this compound crystallizes in the cubic crystal system. The temperature dependence of heat capacity was studied by experimental calorimetry in the range of 298.15–673 K, and it was revealed that on the ~ f(T) curve the compound has anomalous abrupt changes in the heat capacity at 348 and 423 K, probably related to second-order phase transitions. The standard entropy was calculated. The thermodynamic functions S°(T), H°(T) – H°(298.15), and Φxx(T) were calculated in the range of 298.15–675 K. The temperature dependences of electric capacity, electric resistance, and permittivity were studied in the range of 293–483 K, and it was established that NdLi2NiMnO5 has hole conductivity at 293–363 and 423–483 K and metallic conductivity at 363–423 K.
electrophysics , lithium , neodymium , nickelite-manganite , thermodynamics
Text of the article Перейти на текст статьи
Abishev Chemical-Metallurgical Institute, Karagandy, 100009, Kazakhstan
Gumilev Eurasian National University, Astana, 10000, Kazakhstan
Abishev Chemical-Metallurgical Institute
Gumilev Eurasian National University
10 лет помогаем публиковать статьи Международный издатель
Книга Публикация научной статьи Волощук 2026 Book Publication of a scientific article 2026