Effect of the deoxidizer composition on microstructure and strength properties of 30khn2ma steel
Isagulov A.Z. Kvon S.S. Kulikov V.Yu. Alina A.A.
2021Ore and Metals Publishing house
Chernye Metally
2021#2021Issue 638 - 41 pp.
This article examines the effect of the new deoxidizer on the structure and some properties of steel 30KhN2MA. As an experimental deoxidizer, we used ferrosilicoaluminum FS45A15, obtained according to the technology developed by the Chemical-metallurgucal institute named after Zh. Abishev. For metallographic analysis, the Thixomet Pro program was used, while the grain score of the structure and the index of contamination with non-metallic inclusions were assessed. Based on these data, it can be assumed that changes in the microstructure of steel after using a new deoxidizer will lead to some change in mechanical properties. To test this assumption, the prototype was tested for hardness, strength and wear resistance. All tests were carried out in accordance with the relevant GOST. Steel 30KhN2MA, deoxidized in the usual way, was used as a comparative sample-a standard. Experimental smelting was carried out in a modernized induction furnace of the UIP-25 type, ferrosilicoaluminium was introduced into the furnace a few minutes before the end of smelting. After complete cooling, specimens were cut from the mass of the experimental melting for heat treatment. Heat treatment mode: quenching 860°C oil, tempering 400°C air; after heat treatment, thin sections for metallographic analysis were prepared from the prototypes. For metallographic analysis, the Thixomet Pro program was used, while the grain score of the structure and the index of contamination with non-metallic inclusions were assessed. The results of this study show that deoxidation with new ferrosilicoaluminium FS45A15 has a beneficial effect on the formation of a fine-grained structure.
Deoxidation , Ferroalloys , Ferroaluminium , Hardening , Heat treatment , Microstructure , Wear resistance
Text of the article Перейти на текст статьи
Karaganda Technical University, Karaganda, Kazakhstan
Dept. of Nanotechnology and Metallurgy, Karaganda Technical University, Karaganda, Kazakhstan
Karaganda Technical University
Dept. of Nanotechnology and Metallurgy
10 лет помогаем публиковать статьи Международный издатель
Книга Публикация научной статьи Волощук 2026 Book Publication of a scientific article 2026