Enhanced operational reliability of irrigation canals through the application of modified concrete

Повышение эксплуатационной надежности оросительных каналов за счет применения модифицированного бетона
Imanov A.М. Moldamuratov Z.N. Seitkazinov O.D. Tukhtamisheva A.Z. Ismailova A.B. Rakhimova G.M.
2025 Center for New Technologies Nanostroitel

Nanotechnologies in Construction
2025 #17 Issue 6 678 - 696 pp.

Introduction. In the conditions of Southern Kazakhstan, irrigation canals play a crucial role in supplying water for agricultural production. The operation of conventional concrete linings is complicated by their low resistance to cracking, frost heave, abrasive wear, and exposure to aggressive environments. These factors lead to increasing filtration losses, which in some cases exceed 20-25% of the water supplied volume-an especially critical issue for a region characterized by a sharp continental climate and limited water resources. To improve the durability and impermeability of hydraulic structures, a modified concrete (MC) mixture incorporating a combination of mineral and chemical additives has been developed. Materials and Methods. The composition of the MC includes Portland cement and slag-Portland cement, quartz sand, granite coarse aggregate, silica fume (7% of the cement mass), fly ash, an air-entraining agent (0.05%), and hydrophobizing components. The experimental investigations were conducted in accordance with relevant GOST standards: compressive and splitting tensile strength (GOST 10180), frost resistance (GOST 10060), water impermeability (GOST 12730.5), abrasive resistance (GOST 13087), and sulfate resistance (GOST 31384). The micro-and nanostructure of the material was analyzed using SEM, EDS, and XRD methods. Results and Discussion. Compared with the control concrete (CC), the modified concrete demonstrated significant performance improvements: an increase in compressive strength up to 55 MPa (+14.6%) and in splitting tensile strength up to 4.6 MPa (+27.8%); an increase in frost resistance from 220 to 320 cycles (+45%); an improvement in water impermeability from W6 to W9 (+50%); enhanced abrasion resistance by 26.9%; and an increase in the sulfate resistance coefficient by 11.5%. Microstructural analysis revealed densification of the cement matrix, a reduction in macroporosity, and an increase in the content of low-basic C-S-H phases, which confirms the materials enhanced durability. Conclusion. The developed modified concrete exhibits a comprehensive improvement in operational performance, ensuring a 30-40% extension of the service life of canal linings and a reduction in filtration losses by up to 20%. Its implementation in the construction and rehabilitation of irrigation canals in Southern Kazakhstan will enhance water-use efficiency and improve the resilience of hydraulic structures under aggressive environmental impacts and persistent water scarcity.

abrasion resistance , canal lining , frost resistance , micro-and nanostructure , modified concrete , sulfate resistance , water impermeability

Text of the article Перейти на текст статьи

Abylkas Saginov Karaganda Technical University, Karaganda, Kazakhstan
International Educational Corporation, Almaty, Kazakhstan
Kazakh Leading Academy of Architecture and Civil Engineering, Almaty, Kazakhstan

Abylkas Saginov Karaganda Technical University
International Educational Corporation
Kazakh Leading Academy of Architecture and Civil Engineering

10 лет помогаем публиковать статьи Международный издатель

Книга Публикация научной статьи Волощук 2026 Book Publication of a scientific article 2026