Ceramic molds based on yttrium oxide for the casting of titanium alloys
Chukmanova M.T. Panichkin A.V. Mamayeva A.A. Kenzhaliyev B.K. Azlan M.N.
4 July 2023Institute of Metallurgy and Ore Beneficiation JSC
Kompleksnoe Ispolzovanie Mineralnogo Syra
2023#324Issue 171 - 82 pp.
The effect of various binding agents based on aqueous solutions of nitric acid, yttrium nitrate and orthophosphoric acid and yttrium hydroxide gel on the physical and mechanical properties of casting molds based on Y2O3 has been studied. It is shown that the most promising binding agent for yttrium oxide casting molds is a phosphate bond. The data describing the curing mechanism of phosphate-bonded molding mass is presented. The influence of the concentration of binding agent solutions on the strength characteristics of molding materials after curing and heat treatment is shown. Information about the interaction of yttrium oxide powder molds with phosphate-binding with titanium melt of VT1-0 and VT6 grades is presented. The obtained data allowed us to describe the advantages and disadvantages of the developed molding compound. A method for producing casting molds based on yttrium oxide powder with a yttrium phosphate-binding agent was developed based on this research.
binding agent , casting mold , molding mixture , titanium alloy , yttrium oxide
Text of the article Перейти на текст статьи
Institute of Metallurgy and Ore Beneficiation, Satbayev University, Almaty, Kazakhstan
University Pendidikan Sultan Idris, Malaysia
Institute of Metallurgy and Ore Beneficiation
University Pendidikan Sultan Idris
10 лет помогаем публиковать статьи Международный издатель
Книга Публикация научной статьи Волощук 2026 Book Publication of a scientific article 2026