Microstructure and tribological study of TiAlCN and TiTaCN coatings
Bakhytuly N. Kenzhegulov A.K. Nurtanto M. Aliev A.E. Kuldeev E.I.
30 January 2023Institute of Metallurgy and Ore Beneficiation JSC
Kompleksnoe Ispolzovanie Mineralnogo Syra
2023#327Issue 499 - 110 pp.
The low coefficients of friction and wear rates of transition metal carbonitride make them excellent candidates for friction and wear applications. Coatings based on titanium carbonitride alloyed with Ta and Al were deposited using reactive magnetron sputtering on the surface of titanium VT1-0 and steel AISI 304. The effect of alloying titanium carbonitrides with Ta and Al and acetylene flow during deposition on the structure, composition, and tribological properties of the coating was studied. TiAlCN and TiTаCN coatings were deposited in various acetylene flows along with stable argon and nitrogen flows. Scanning electron microscopy, optical microscopy, X-ray phase analysis, and sliding wear test (ball-on-disk method) in two media were used to study the resulting coatings. The average coefficient of friction of the coating under friction without lubrication varied in the range of 0.13-0.85 and under friction with lubrication in the range of 0.0015-0.081. From the point of view of wear rate, it is shown that the most wear resistant coating under friction conditions with and without lubrication is TiAlCN-2. The resulting coatings can be useful as protection for machine parts or tools that are subject to friction and wear.
alloying , coefficient of friction , magnetron sputtering , titanium carbonitride , wear rate , wear resistance
Text of the article Перейти на текст статьи
JSC Institute of Metallurgy and Ore Beneficiation, Satbayev University, Almaty, Kazakhstan
University of Sultan Ageng Tirtayasa, Banten, Indonesia
University of Texas, Dallas, TX, United States
JSC Institute of Metallurgy and Ore Beneficiation
University of Sultan Ageng Tirtayasa
University of Texas
10 лет помогаем публиковать статьи Международный издатель
Книга Публикация научной статьи Волощук 2026 Book Publication of a scientific article 2026