ANALYSIS OF A NEW FILAMENT MAKING MEL PRESSING DEVICE
Absadykov B.N. Bazarbay B.B. Isametova M.E. Mashekova A.S.
2022National Academy of Sciences of the Republic of Kazakhstan
News of the National Academy of Sciences of the Republic of Kazakhstan, Series of Geology and Technical Sciences
2022#2022Issue 46 - 15 pp.
The filament for Fused Deposition Modeling technology was deve-lo ped in a new melt pressure pressing device using metal-polymer composite material. Phase analysis of metal-polymer composite material was carried out by X-ray di fraction. The material was subjected to XRD analysis in the 2θ, 3–90° range, and in Cu Kα radiation at 1.5408 Å and a pitch of 0.02° on a Rigaku MiniFlex. Thermogravimetric analysis was carried out in a Perkin Elmer Pyris instrument at a temperature range of 0 °C – 512.6 °C under a nitrogen atmosphere of 40 mL/min by volume. It was studied at what temperature the heaters in this device should be maintained. In addition, it was found that the metal powders contained in the metal-polymer composite material can be changed to adhesive powders by mechanical compression under a pressure of 18 MPa. The research was carried out under the grant No. AP08857034.
filament , New press device , Thermogravimetric analysis , XRD analysis
Text of the article Перейти на текст статьи
Satbayev University, Almaty, Kazakhstan
Satbayev University
10 лет помогаем публиковать статьи Международный издатель
Книга Публикация научной статьи Волощук 2026 Book Publication of a scientific article 2026